Microscopy providers by MicroVision Laboratories, Inc. 2021? Problem: A client was a manufacturer of beverages, bottled water, and other drinks. They received a customer complaint through one of their distributors, which indicated that a customer had been drinking a bottle of water, and as they neared the bottom of the bottle, found a mysterious white powder floating in the bottom. The customer returned the bottle and complained. The client hoped to identify the powder so they could both satisfy their end customer, as well as identify any potential problems in their manufacturing or bottling process.
SEM allows for high magnification surface examinations of a wide variety of samples. Providing brilliant resolution as well as incredible depth of field, the SEM, especially when combined with EDS, is often considered the most powerful analytical tool of our time. Let us show you why. X-ray imaging allows us to look inside of a device without opening it up. This real-time nondestructive inspection technique can be used on packaged electronic devices to one of a kind ancient artifacts. With rapid image acquisition and high sample throughput, X-ray imaging is particularly useful for sample screening and quality control issues. It is also often the first step in failure analysis and polished cross section projects.
What if I want a service not listed in your services list? At MicroVision Labs the list of services which we provide to our clients is constantly growing. So if you don’t see what you are looking for give us a call or use the Contact Us tab. Also don’t forget to check our Additional Services Page to see if it might be listed there. Can you identify a contamination or unknown for us? Yes, we call that an Unknown Material ID and we routinely work on that kind of project. We have a number of individual tests designed to classify unknown materials. When combined with our extensive suite of equipment, these tests allow us to identify virtually any material. Give us a call and talk to one of our knowledgeable staff for more information. Explore a few more info on source. ?We partner with companies in all phases of product development and sales, including R&D, manufacturing, QC, advertising and failure analysis. Our laboratory offers a highly-trained and experienced staff utilizing a powerful set of analytical tools (SEM with EDS and backscatter detectors, Bruker X-Flash elemental mapping, X-Ray imaging, Micro-FTIR spectroscopy, Micro-XRF, light microscopy, cross sectioning/precision polishing and microhardness testing).
The data indicated that a significant portion of the dust was from the insulation in the attic. The contractor had replaced a portion of duct work running to the master bedroom. During this replacement, fiberglass insulation was knocked into the ducting. The small glass insulation fibers were spread through the AC ducts and settling out of the air throughout the house. The client was relieved to know what was causing their skin irritation and the significant dust build up. Using the results garnered from the analysis from MicroVision Labs they were able to have the contractor clean out the duct work and act to prevent further spread of the insulation fibers and properly clean up the settled dust in the house that was the cause of the homeowner’s skin irritation.
The profile of the flow of the solder at these bonds was documented using the SEM with backscatter imaging, which correlates brightness in the image with atomic density. Some voids were found in the solder as shown the SEM image. An EDS spectrum of the solder was acquired which showed that the solder was a tin/lead (80/20) solder. The EDS map clearly shows the copper wire and copper pad (red) with the tin lead solder (light blue) that appears to have flowed well and made a good bond between the copper elements. This map also shows the fiberglass bundles that add structural integrity to the board. See more details at https://microvisionlabs.com/.