Ftir analysis and elemental mapping services in Chelmsford? Conclusion: Based on the analytical report, the client was able to demonstrate that the particles were consistent with a common aspirin tablet. When the end customer was approached with this report, they remembered that their spouse had taken an aspirin earlier that morning, and had likely used the bottle of water in question to do so. Based on this, the customer was happy, the manufacturing client was satisfied, and the sample was maintained – undestroyed should someone need to examine the sample again or do any more esoteric testing. For an affordable price, the client was able to get piece of mind, and gather information from a very wide range of testing methods quickly and accurately.
SEM allows for high magnification surface examinations of a wide variety of samples. Providing brilliant resolution as well as incredible depth of field, the SEM, especially when combined with EDS, is often considered the most powerful analytical tool of our time. Let us show you why. X-ray imaging allows us to look inside of a device without opening it up. This real-time nondestructive inspection technique can be used on packaged electronic devices to one of a kind ancient artifacts. With rapid image acquisition and high sample throughput, X-ray imaging is particularly useful for sample screening and quality control issues. It is also often the first step in failure analysis and polished cross section projects.
Do you do any animal testing? No. Do you analyze any tissue samples or blood samples? No. We do not do any blood analyses and we are not set up to prepare tissue samples. What are some of the cool samples you have looked at under the scanning electron microscope? We have seen 10,000 year old Wolly Mammoth hair, meteorites, an artificial heart valve, civil war bullets, insulin pumps, rare colonial coins, a kidney stone, and a few things we can’t talk about. But some of the more mundane samples, like wood or salt crystals, have proven to be extremely interesting subjects to image. Discover a few extra info on this website.
The scan from left to right shows a high tin concentration (green line) while areas of higher lead concentrations (blue line) were not intersected by the line scan. At the interface between the tin/lead solder and copper (red line), there is a mixture of the solder and copper which is the intermetallic layer. The EDS Map provides a nice visual mixture of colors which shows the intermetallic layer while the line scan clearly shows the intermetallic with the elemental graph.
?We partner with companies in all phases of product development and sales, including R&D, manufacturing, QC, advertising and failure analysis. Our laboratory offers a highly-trained and experienced staff utilizing a powerful set of analytical tools (SEM with EDS and backscatter detectors, Bruker X-Flash elemental mapping, X-Ray imaging, Micro-FTIR spectroscopy, Micro-XRF, light microscopy, cross sectioning/precision polishing and microhardness testing).
The data indicated that a significant portion of the dust was from the insulation in the attic. The contractor had replaced a portion of duct work running to the master bedroom. During this replacement, fiberglass insulation was knocked into the ducting. The small glass insulation fibers were spread through the AC ducts and settling out of the air throughout the house. The client was relieved to know what was causing their skin irritation and the significant dust build up. Using the results garnered from the analysis from MicroVision Labs they were able to have the contractor clean out the duct work and act to prevent further spread of the insulation fibers and properly clean up the settled dust in the house that was the cause of the homeowner’s skin irritation. Discover more info at https://microvisionlabs.com/.